Technical Data

Technical Data

Engineering plastics

Acronym

Food contact

Density

Coefficient of friction

Rockwell hardness

Minimum working temperature

Maximum working temperature

Water absorption to saturation

Tensile stress at yield

Elongation at break

Flamability

(kg/m3) mU R M D Continuous (°C) (%) (N/mm²) % UL94
Acetal co-polymer POM-C Y 1410 0.25 103 84 85 -45 110 0.8 65 66 HB
Acetal homo-polymer POM-H Y/N 1430 0.20 116 88 -45 110 1.0 78 35 HB
Cast Nylon 6 PA6 C Y/N 1150 0.36 114 88 82 -40 100 6.5 82 25 HB
Cast Nylon 6+ heat stabilised PA6 HS N 1150 0.30 109 87 84 -40 115 6.5 82 25 HB
Cast Nylon 6 + MOS2 MOS2 N 1150 0.25 112 84 85 -40 105 6.2 82 30 HB
Cast Nylon 6 + oil filled OILON N 1140 0.15 82 83 -40 110 6.0 75 30 HB
Extruded Nylon 6 PA6 E Y/N 1140 0.38 85 -40 85 9.0 76 50 HB
Extruded Nylon 66 PA6.6 E Y/N 1140 0.34 115 88 -30 95 8.0 90 50 HB-V2
Extruded Nylon 66 + Glass filled 30% PA6.6 GF30 N 1300 0.33 76 -20 120 5.5 5 HB
Extruded Nylon 66 + MOS2 PA6.6 MOS2 N 1150 0.25 88 -20 80 7.8 92 20 HB
Polyethylene 1000 Virgin Natural PE1000N Y 950 0.20 62 -200 80 0.0 20 300 HB
Polyethylene 1000 REGEN PE1000R N 950 0.20 62 -200 80 0.0 20 300 HB
Polyethylene 1000 Ceram P CeramP N 950 0.20 65 -200 80 0.0 20 300 HB
Polyethylene 1000 ESD PE1000ESD N 950 0.20 64 -200 80 0.0 20 300 HB
Polyethylene 500 HMWPe Y 950 0.25 65 -75 80 0.0 20 300 HB
Polycarbonate PC Y 1200 0.58 75 85 -30 120 0.4 75 60 HB
Polyethylene Terephthalate (Polyester) PET-P Y 1390 0.20 112 92 -20 115 0.5 90 15 HB
Polypropylene co-polymer PP-C Y 1000 0.32 97 73 -10 90 0.0 30 100 HB
Polytetrafluroethylene PTFE Y 2180 0.10 57 -200 260 0.0 27 200 None
  • Other materials and sizes are available on request