Esband NE Types

Esband NE Types

Esband type Surface options Tensile element Coating/hardness Colours Breaking strength per cm endless Smallest pulley dia. Permissible open temp. continuous Thickness(mm)
NE Mini – Profiled on one side
– Smooth on one side
Polyester Polychloroprene
75 ±5 ShA
Black 550N 6mm -20 to +100°C 0.5
NE 10 – Profiled on one side
– Smooth on one side
Polyamide/Polyester Polychloroprene
75 ±5 ShA
Black 750N 8mm -20 to +100°C 0.8
NE 10/133 – Profiled or smooth on one side
– Second side textile impregnated
Polyamide/
Polyester
Polychloroprene
75 ±5 ShA
Black 700N 8mm -20 to +100°C 0.7
NE 17 – Profiled on one side
– Smooth on one side
– Ground on both sides
Aramid Polychloroprene
75 ±5 ShA
Black 2400N 12mm -20 to +100°C 0.9
NE 17/133 – Profiled or smooth on one side
– Second side textile impregnated
Aramid Polychloroprene
75 ±5 ShA
Black 2400N 12mm -20 to +100°C 0.8
NE 18 – Profiled on one side
– Smooth on one side
– Ground on both sides
Aramid Polychloroprene
75 ±5 ShA
Black 7950N 30mm -20 to +100°C 2.0
NE 18 GA V 10535 Ground on both sides Aramid Polychloroprene
75 ±5 ShA
Black 11340N 50mm -20 to +100°C 3.0
NE 20 – Profiled on one side
– Smooth on one side
Polyester/
Cotton
Polychloroprene
75 ±5 ShA
Black 950N 10mm -20 to +100°C 0.8
NE 21 – Profiled on one side
– Smooth on one side
– Ground on both sides
Polyester Polychloroprene
75 ±5 ShA
Black 1700N 15mm -20 to +100°C 0.9
NE 22 – Profiled on one side
– Smooth on one side
– Ground on both sides
Polyester Polychloroprene
75 ±5 ShA
Black 3400N 20mm -20 to +100°C 1.4
NE 26 – Profiled on one side
– Smooth on one side
– Ground on both sides
Polyester Polychloroprene
75 ±5 ShA
Black 4150N 25mm -20 to +100°C 2.0
NE Elastic Ground Without carcass Polychloroprene
75 ±5 ShA
Black On request 5mm -20 to +100°C 0.8-0.5