BRECO® Backed Belts
| Material | Description | Thickness | Temp range | Min. pulley dia |
|---|---|---|---|---|
|
Ausf-T
|
85 Shore ‘A’ polyurethane material is a highly abrasion resistant backing with good cut and tear resistance. Good resistance against simple oils and fats. | 2mm | to 80°C | 80mm |
|
NP
|
85 Shore ‘A’ polyurethane material is a highly abrasion resistant backing with good cut and tear resistance. Good resistance against simple oils and fats. Has a profiled ‘pimple’ surface. | 4mm | to 80°C | 80mm |
|
FG
|
85 Shore ‘A’ polyurethane material is highly abrasion resistant backing with good cut and tear resistance. Good resistance against simple oils and fats. Has a profiled herringbone’ surface. | 4mm | to 80°C | 120mm |
|
Sylomer
|
85 Shore ‘A’ polyurethane material with a high coefficient of friction is highly abrasion resistant with good cut and tear resistance. Good resistance against petrol, simple oils and fats. | 3mm 4mm 5mm 6mm |
to 80°C | 80mm 120mm 150mm 180mm |
|
Sylomer
|
Low to medium density partially closed cell elastomer for conveying delicate items. Good oil, grease, solvent and general chemical resistance. Good abrasion resistance. Available in three increasing densities, brown, green and blue | 12mm 25mm 12mm 25mm 12mm 25mm |
to 80°C | 80mm 120mm 80mm 120mm 80mm 120mm |
|
PU-Yellow
|
Very high density fully closed cell elastomer for conveying delicate items. Good oil, grease, solvent and general chemical resistance. High wear resistance. Good for vacuum belts. | 3mm 4mm 5mm |
to 60°C | 60mm 80mm 100mm |
|
Supergrip
|
Green and blue approx. 30 Shore ‘A’ PVC profiled backing with good resilience and high wear resistance. The green is oil and fat resistant and suitable for snack food conveying applications. The blue PVC is not oil resistant. | 4mm 4mm |
to 60°C | 60mm 60mm |
|
Porol
|
Black closed cell polychloroprene sponge. Good aging, oil, compression and chemical resistance and nonliquid absorbent. Non flammable and self extinguishing. | 2mm 3mm |
to 60°C | 40mm |
|
Celloflex
|
Polyurethane foamed elastomer with micro cellular construction. Excellent wear resistance. Good resistance against simple oils and fats. Very flexible. | 2mm 3mm 5mm |
to 80°C | 80mm |
|
HV-1-Film
|
Transparent PU film suitable for food contact with good wear resistance and resistance to some cleaning agents. | 1mm | to 60°C | 80mm |
|
Chrome Leather
|
Grey/blue chrome leather backing resistant to simple oils and fats. Good friction coefficient and resistant to abrasion. Good for conveying oily or greasy components. | 2mm 3mm |
to 60°C | 80mm 100mm |
|
Viton
|
Black 75 Shore ‘A’ fluoroelastomer mix material with high contact temperature resistance up to 200°C. Resistant to simple oils and greases. Suitable for short term conveying of parts having a high residual temperature | 2mm | to 200°C | 80mm |
|
Correx
|
Filled natural rubber excellent for profiling and grooving. High tear and abrasion resistance. High resilience and elasticity. Good for general conveying duties.. | 6mm 10mm |
to 70°C | 80mm 120mm |
|
Linatex
|
Approx. 40 Shore ‘A’ natural rubber is the most common and versatile backing material with outstanding resilience and remarkable cut and tear resistance. Excellent wet abrasion resistance. Not oil and grease resistant. | 2mm 3mm 4mm 5mm 6mm 8mm 10mm |
to 60°C | 60mm 80mm 80mm 80mm 100mm 100mm 120mm |
|
PVC White
|
Approx. 40 Shore ‘A’ white PVC. Resistant to oils and fats and FDA approved for contact with foodstuffs. | 2mm 3mm 4mm 5mm 6mm |
to 80°C | 60mm 60mm 80mm 120mm |
|
PVC Herringbone
|
Approx. 40 Shore ‘A’ white PVC. Resistant to oils and fats and FDA approved for contact with foodstuffs. Top surface has ‘herringbone’ pattern. | 4mm | to 80°C | 80mm |
|
PVC Blue
|
Approx. 40 Shore ‘A’ blue PVC. High coefficient of friction. Resistant to some oils and fats. | 1mm | to 80°C | 30mm 30mm |
|
PVC Minigrip
|
Approx. 40 Shore ‘A’ blue PVC.Textured top surface. High coefficientof friction. Resistant to some oils and fats. | – | to 80°C | 30mm |
|
PAZ
|
Low coefficient of friction nylon tooth facing. Resistant to some oils and fats. | – | to 80°C | – |
|
PAR
|
Low coefficient of friction nylon back facing. Resistant to some oils and fats. | – | to 80°C | – |
|
PAZ/PAR
|
Low coefficient of friction nylon tooth and back facing. Resistant to some oils and fats. | – | – |